| Product Name: Styrene Butadiene Copolymer (Rubber) Trade Name: SBR Producer: KUMHO |
Overview
SBR is produced with the patent technique licensed from Zeon, Japan. The Whole set of unit was designed and provided by Mitsubishi Heavy Industries, Ltd. With butadiene and styrene as main feedstock, SBR are produced by low temperature (5 ℃) emulsion polymerization procedures. Compared with natural rubber, SBR possess outstanding abrasion-, ageing-, ozone-, water-resistance, air-tightness and homogeneity characteristics and could be blended with natural rubber in any proportion.
Production plant
The Styrene Butadiene Rubber plant at the Qilu Company has a production capacity of 250kta. The products are respectively brand-named SBR1500, SBR1502, SBR1712, etc.
|
Specification of SBR ITEM |
SBR1500 |
SBR1502 |
SBR1712 |
|
Volatiles % |
≤1.30 |
≤0.90 |
≤1.00 |
|
Ash % |
≤1.50 |
≤0.50 |
≤0.50 |
|
Organic Acid % |
3.90-7.25 |
4.50-6.75 |
3.90-5.70 |
|
Soap % |
≤0.50 |
≤0.50 |
≤0.50 |
|
Bound Styrene % |
22.5-24.5 |
22.5-24.5 |
22.5-24.5 |
|
Oil content % |
— |
— |
24.3-30.3 |
|
Raw Viscosity ML(1+4)100 |
45-59 |
44-56 |
42-56 |
|
Compound Viscosity ML(1+4)100 |
≤88 |
≤93 |
≤70 |
|
300% Modulus 145℃ 25min MPa |
— |
15.5±2.5 |
9.3-14.3 |
|
300%Modulus 145℃ 35min MPa |
14.2-20.2 |
20.6±2.5 |
11.6-16.6 |
|
300%Modulus 145℃ 50min MPa |
— |
21.5±2.5 |
12.5-17.5 |
|
Tensile Strength 145℃ 35min MPa |
≥19.6 |
≥24.5 |
≥18.4 |
|
Elongation at break 145℃ 35min % |
≥570 |
≥330 |
≥370 |
Packaging
SBR is packed in internal PE coated plastics woven bags with 35 kg each for net or packed in goodpack with 1260 kg each.
Transportation and storage
SBR should be stored in dry and well ventilated warehouse at ambient temperature. Precautions should be taken against sunburn or rainwater in transportation and handling. Vehicle should be clean and damaged packaging materials should be prevented from entering.